NewsCurrent Position : Home > News > TM52 is not recommended for High Chromium Wear Parts
News

TM52 is not recommended for High Chromium Wear Parts

Author: langfeng Time: 2017-03-01

Recently, many customers inquired whether high chromium wear parts could use TM52 steel bonded TiC cermets inserts . As our experience, it is not recommended.

Our TiC cermets inserts has the similar thermal expansion coefficient as base material:13% high manganese steel . When the surface of tic rods be melted, two materials will be bonded together perfectly. There is no need to worry about the problem of "drop out ".

And this properity is not working for high chromium wear part.

Basing on this, we do not recommend.

If you have any more idea in steel casting, please feel free to cotact us via : sales@langfengmaterials.com

 

Prev Article:TiC TaC Cost Rise

Next Article: TM60 and Its Application

Online Message
If you have any suggestions or opinions about our products,please leave a message,and we will immediately answer your questions. Thanks for your support.
Your Name:
* Your E-mail:
* Message: